13MnNiMo5-4 Hot Rolled Pressure Vessel Steel Plate Normalized And Tempered

Product Details:
Place of Origin: China
Brand Name: VANFORGE
Certification: ISO9001:2015, ABS, BV, CCS, DNV GL, NKK
Payment & Shipping Terms:
Minimum Order Quantity: 5 metric tons
Price: Negotiable
Packaging Details: In bundles, standard seaworthy packing for export
Delivery Time: 15 days
Payment Terms: L/C, T/T
Supply Ability: 3000 metric tons per month

Detail Information

Material: Low Alloy Steel Process: Hot Rolled
Shape: Flat Plate Surface Treatment: Plain And Smooth
Length: Up To 12000mm Condition: Normalized And Tempered
Application: Structure Feature: High Weldability
High Light:

structural steel sheet

,

hr steel plate

Product Description

13MnNiMo5-4 normalized and tempered fine grain pressure vessel steel plate

 

13MNNIMO5-4 PRESSURE VESSEL STEEL is a weldable steel for higher temperature service. It is characterized by high 0.2% proof stress at elevated temperatures. 13MNNIMO5-4 PRESSURE VESSEL STEEL is produced using basic oxygen steelmaking process. Its properties are achieved by normalizing and tempering. It is used as plate or formed part for boilers, pressure vessels, piping and other fabricated parts operating at temperatures up to 400 °C.

 

Product description

Range of application

13MNNIMO5-4 PRESSURE VESSEL STEEL is material No. 1.8807. In Germany, it is defined as

13MnNiMo5-4 in VdTÜV-material data sheet 384 for supervised installations e.g. for pressure vessel installations in accordance with the AD-2000 Merkblätter for temperatures from -10 °C up to 400 °C.

 

Application according to corresponding standards has to be checked for each separate case.

This material specification applies to heavy plates with thicknesses from 6 to 150 mm; higher thicknesses can be agreed upon.

 

Chemical analysis in %, max.

C Si Mn P S Ni Mo Cr Nb Al
0.17 0.05-0.56 0.95-1.70 0.025 0.004 0.55-1.05 0.15-0.44 0.15-0.45 0.025 0.015

Fully killed, fine grained steel with metallurgical treatment in the ladle.

 

Delivery condition

Normalized and tempered, unless otherwise agreed.

 

Mechanical properties in the delivery condition

Tensile test at ambient temperature (transverse test specimens)

Plate thickness

[mm]

Yield strength ReH

[MPa], minimum

Tensile strength Rm

[MPa]

Elongation A5

%, minimum

≤ 50 400 570-740 18
> 50 ≤ 100 390 570-740 18
> 100 ≤ 125 380 570-740 18
> 125 ≤ 150 375 570-740 18

For thicknesses > 150 mm values have to be agreed upon in the state of inquiry.

 

Improved deformation properties perpendicular to the surface

For plate thicknesses * 15 mm, the fulfillment of one of the three quality classes Z15, Z25 or Z35 in accordance with EN 10164 or similar rules can be stipulated on the order. These quality classes correspond to a minimum reduction of area on through-thickness tensile test specimens of 15, respectively 25, respectively 35 % (minimum value for the average of 3 tests).

 

0.2% proof stress at elevated temperatures (transverse test specimens)

Plate thickness Minimum yield strength Rp0,2 [MPa] at test temperature
[mm] 100 °C 200 °C 250 °C 300 °C 350 °C 400 °C
≤ 50 393 378 373 363 353 309
> 50 ≤ 100 373 358 353 343 333 304
> 100 ≤ 125 363 348 343 333 324 299
> 125 ≤ 150 353 338 333 324 314 294

For thicknesses > 150 mm values have to be agreed upon in the state of inquiry.

 

Impact test with Charpy-V transverse specimens

Test temperature in °C 0 20
Minimum impact value in J 31 39

 

The specified value is the minimum value for the average of 3 tests. No individual value is to be less than 70% of the specified minimum. For boiler drum plates no individual value is to be less than 85% of the specified minimum.

 

In case of application for boiler drums this is to be agreed on the inquiry. For plate thicknesses below 10 mm the test will be carried out on Charpy-V-type specimens with reduced width. The minimum impact value will be reduced proportionally to the reduction of the specimens' cross section.

 

Testing

Sampling, testing method and tests are in accordance with the provisions in EN 10028 and VdTÜV-material data sheet 384 except that, unless otherwise agreed, the 0.2% proof stress test at elevated temperatures is carried out at 350 °C and 400 °C instead of 300 °C The plates are delivered with inspection certificate 3.2 or 3.1 in accordance with EN 10204. The document type and, in case of inspection certificate 3.2, the inspection representative are to be stated on the order.

 

Identification of plates

Unless otherwise agreed the marking is carried out with low stress steel stamps with at least the following information:

• steel grade (13MNNIMO5-4 PRESSURE VESSEL STEEL)

• heat number

• number of mother plate and individual plate

• the manufacturer's symbol

• authorized inspection representative’s sign

 

Fabrication properties

The entire processing and application techniques are of fundamental importance to the reliability of the products made from this steel. The user should ensure that his design, construction and processing methods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply with and are suitable for the intended use. The customer is responsible for the selection of the material. The recommendations in accordance with EN 1011-2 should be observed.

 

Forming properties and weldability

13MNNIMO5-4 PRESSURE VESSEL STEEL can be hot or cold formed and can be welded and flame cut according to the general procedures. The guidelines according to EN 1011-2 and VdTÜV-material data sheet 384 shall be observed. Welding conditions should lead to cooling time t8/5 10 - 30 s. For more detailed information please refer to our brochure

"Technical Information 13MNNIMO5-4 PRESSURE VESSEL STEEL".

 

Heat treatment

Normalizing 1) Tempering 1) Stress relieving
870-950 °C 580-690 °C 530-600 °C 2)
After equalization over the whole section holding time: After equalization holding time at least 30 min, but not exceeding 180 min.

Thickness

mm

Time 3)

min

15 min for t ≤ 50 mm Cooling in still air ≤ 15 ≥ 15
30 min for t > 50 mm Cooling in still air > 15 ≤ 30 ≥ 30
Cooling in still air Cooling in still air > 30 ≤ 150 about 60

 

1) Temperatures and times are concerning the product.

2) Where the stress relief temperature has to be above 580 °C this has to be clarified in the state of inquiry.

3) Normally the maximum holding time shall be restricted to 150 min. If the holding time exceeds 90 min or in case of repeated heat treatment the lower range of recommended temperatures shall apply. If stress relieving and tempering are joined together in one process, the tempering conditions apply.

 

Temperatures and holding time are determined by the steel manufacturer as a function of the plate thickness and the chemical composition. In order to preserve the mechanical properties the fabricator should ensure that the subsequent heat treatments correspond to those applied by the manufacturer (indicated in the plate inspection document).

 

General technical delivery requirements

Unless otherwise agreed, the general technical delivery requirements in accordance with EN 10021 apply.

 

Tolerances

Unless otherwise agreed, tolerances are in accordance with EN 10029, with class B for the thickness and class N for the flatness.

 

Surface condition

Unless otherwise agreed, the provisions in accordance with class B2 of EN 10163 are applicable.

 

General notes

If special requirements, which are not listed in this material specification, are to be met by the steel due to its intended use or processing, these requirements are to be agreed before the order.

 

 
Production process
13MnNiMo5-4 Hot Rolled Pressure Vessel Steel Plate Normalized And Tempered 0
 
13MnNiMo5-4 Hot Rolled Pressure Vessel Steel Plate Normalized And Tempered 1
 
 

Get in touch with us

Enter Your Message

You Might Be Into These