Umbilical Seamless Capillary Coiled Tubing Super Duplex Stainless 2507
|Place of Origin:||China|
|Certification:||ISO9001:2015, PED 97/23/EC|
|Model Number:||3/8'' OD x 0.065'' WT|
Payment & Shipping Terms:
|Minimum Order Quantity:||10000 feet|
|Packaging Details:||Level wound coiled on wooden spool, and wooden case packing|
|Delivery Time:||10 days (for our required MOQ)|
|Payment Terms:||L/C, T/T|
|Supply Ability:||150000 meters per month|
|Material:||TP316L Comply With NACE MR0175/ISO15156||Tube Type:||Seamless|
|Condition:||Bright Annealed||Length:||Up To 10000 Meters Long Per Reel|
|Qualification:||Hydrostatic Tested||Application:||Oil And Gas Fields|
|Surface:||Metallic Bright||Specialty:||High-pressure Hydraulic|
annealed stainless steel tubing,
stainless steel coil tubing
TP316L Stainless Steel Seamless Pipe Control Line High Strength For Oilfields
TP316L, Chemical composition
Application: Standard oil and gas CRA (corrosion resistant alloy)
Tensile strength, min.: 70ksi (485MPa)
Yield strength, min.: 25ksi (170MPa)
Elongation in 2 in., min.: 35%
TP316L is a chromium-nickel austenitic stainless steel with an addition of molybdenum and reduced carbon content. The addition of molybdenum provides improved resistance to pitting and crevice corrosion in environments containing halides such as chlorides when compared to so-called conventional 18 chromium 8 nickel austenitic stainless steels such as 304L. The reduced carbon content minimizes harmful chromium carbide precipitation during welding and thereby improves resistance to intergranular corrosion. Austenitic stainless steels such as TP316L are susceptible to stress corrosion cracking (SCC) in environments containing chlorides and other halides. TP316L is generally used in oil and gas production environments which do not contain oxygen and have limited amounts of chlorides and hydrogen sulfide. Consult ISO 15156-3, Table A.2 for the limits regarding TP316L in hydrogen sulfide-containing environments for oil and gas production.
HYDRAULIC CONTROL LINE APPLICATIONS
STAINLESS STEEL AND HIGH NICKEL ALLOYS COILED TUBING SOLUTIONS
MEILONG is an important manufacturer in premium coiled seamless & welded tubular solutions for oil and gas applications. In an endeavor to increase its presence in subsea, MEILONG has extended its offer by developing a highly innovative tubular solution for umbilical projects.
MEILONG has developed a strong and unique expertise in premium quality tubes to answer the most stringent specifications of its customers. Based on this expertise in high pressure, and extremely high pressure tubes, MEILONG’s state-of-art factory is exclusively dedicated to the manufacturing and supply of super duplex and high nickel alloys tubes for corrosive downhole applications and is now ready to offer the highest specifications for your toughest challenges.
High quality polymeric jackets/encapsulations provide added protection
Core tubing is evaporated with the latest thermoplastic elastomeric compounds designed to outlast the life of most project tubing installations by reducing the possibility of corrosion and mechanical damage. They can stand up to a wide range of chemical inhibitors and seawater. Most jackets are manufactured from fire retardant, all-weather, abrasion-resistant compound, designed to remain strong and flexible through wide ranges of temperatures and pressures.
● Organic acids at high concentrations and moderate temperatures
● Inorganic acids, e.g. phosphoric and sulphuric acids, at moderate concentrations and temperatures. The steel can also be used in sulphuric acid of concentrations above 90% at low temperature.
● Salt solutions, e.g. sulphates, sulphides and sulphites
● Caustic environments
Austenitic steels are susceptible to stress corrosion cracking. This may occur at temperatures above about 60°C (140°F) if the steel is subjected to tensile stresses and at the same time comes into contact with certain solutions, particularly those containing chlorides. Such service conditions should therefore be avoided. Conditions when plants are shut down must also be considered, as the condensates which are then formed can develop conditions that lead to both stress corrosion cracking and pitting.
TP316L has a low carbon content and therefore better resistance to intergranular corrosion than steels of type TP316.
Standards and Specifications
ASTM A269, Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service
Meets the material limits for TP316L austenitic stainless steel listed in ISO 15156-3, Table A.2
Welded & Redrawn Tubing
Strip splice welds join lengths of cold rolled strip to enable long lengths between orbital welds (greater than 14,500 ft between orbital welds is achievable). The strip is formed into a tubular cross section and longitudinally seam welded using the gas tungsten arc (GTAW) process. The tubing is first sunk to an intermediate outside diameter, heat treated, and make the same process to obtain the desired size.
Seamless & Redrawn Tubing
Seamless extruded tube hollows are drawn or drawn / sunk to final size to produce seamless tubing coils 500 to 2,000 ft. long, depending upon the size. The tubing is heat treated and joined by orbital welding to achieve the desired length. The final material condition of the tubing is heat treated.
Standards and Specifications
Tubing Specification PTM-TS-011, Duplex Stainless 2205 Tubing for Control Line Applications
ASTM A789, Standard Specification for Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing for General Service
Eddy current test (ECT)
Chemical composition analysis
Dimension & visual inspect
Coiled Encapsulated Tubing (Bare Tubing Size)
|Imperial size||Metric size|
Tubing length up to 32,808 feet (10,000 m)
For control line, chemical injection line, umbilicals
Duplex: S31803, S32205
Super Duplex: S32750
Nickel alloy: N06625, N08825
|Grade||UNS No||Euro norm||Japanese|