450HBW Structural Steel Plate Low Alloy Steel High Hardness Full Hard
|Place of Origin:||China|
|Certification:||ISO9001:2015, ABS, BV, CCS, DNV GL, NKK|
Payment & Shipping Terms:
|Minimum Order Quantity:||5 metric tons|
|Packaging Details:||In bundles, standard seaworthy packing for export|
|Delivery Time:||15 days|
|Payment Terms:||L/C, T/T|
|Supply Ability:||3000 metric tons per month|
|Material:||Low Alloy Steel||Process:||Hot Rolled|
|Shape:||Flat Plate||Surface Treatment:||Plain And Smooth|
|Length:||Up To 12000mm||Condition:||Quenched And Tempered|
hr steel plate,
hardened steel plate
S690QL is a high strength quenched and tempered, fine grained structural steel with a minimum yield strength of 690 MPa (100 ksi)2 in its delivery condition (referring to the lowest thickness range).
S690QL is preferentially used for welded steel structures within mechanical constructions, plant constructions and structural steel works, such as machines for structural engineering, conveying plants, hoists, cranes, flood gates, bridges and frameworks.
Designation and range of application
S690Q can be delivered in following quality:
Tough (T) with minimum impact values at 40 °C (-40 °F)2:
Material No. 1.8928 - S690QL according to EN 10025-6
S690QL can be delivered as basic grade (B) or tough grade (T) in thicknesses from 6 to 255 mm (¼ to 10 in.)2, as extra tough grade (E) in thicknesses from 6 to 200 mm (¼ to 8 in.)2 according to the dimensional program.
S690QL fulfils all requirements of EN 10025-6. If a CE marking according to EN 10025-1 is needed, an additional attestation for the corresponding quality according to EN 10025-6 has to be ordered.
For the ladle analysis, the following limiting values in % are applicable, max.:
|t > 200mm||0.18||0.50||1.60||0.018||0.005||1.50||2.60||0.70||0.10||0.004|
The steel is fine grained through sufficient aluminium content.
Water quenched and tempered according to EN 10025-6.
Tensile test at ambient temperature – transverse test pieces –
Plate thickness t [mm]
Rmb [MPa] (ksi)a
Minimum yield strength
ReHb,c [MPa] (ksi)a
|A5b [%]||A2in.b,d [%]|
|t ≤ 65 (2.5)||770 – 930 (112 – 136)||690 (100)||141||15|
|65 (2.5) < t ≤ 100 (4)||770 – 930 (112 – 136)||670 (97)||14||15|
|100 (4) < t ≤ 150 (6)||720 – 900 (104 – 130)||630 (91)||14||15|
|150 (6) < t ≤ 200 (8)||700 – 880 (102 – 128)||610 (88)||141||15|
|200 (8) < t ≤ 255 (10)||690 – 870 (100 – 126)||600 (87)||14||15|
a The approximately converted values in brackets are for information only.
b Higher minimum values may be agreed on request. For Offshore applications special grades are available.
c If not apparent, the yield strength Rp0.2 is measured instead.
d These values apply if tested according to ASTM A370.
Impact test on Charpy-V-specimens
|Specimen direction||Impact energy KV2 [J] (ft.-lb.)a at test temperature b|
|Tough (T)||longitudinal/transverse in addition:||
30/27 (22/20) at -40 °C (-40 °F) according to EN 10025-6
60/40 (44/30) at -40 °C (-40 °F) in thickness up to 120 mm
a) The approximately converted values in brackets are for information only.
B) Enhanced impact energy requirements can be agreed upon request. For offshore applications special grades are available. The specified minimum value is the average of 3 tests. One individual value may be below the minimum average value specified, provided that it is not less than 70 % of that value. For plate thicknesses below 12 mm, the test can be carried out on Charpy-V test pieces with reduced width; the minimum width must be 5 mm. The minimum impact value will be decreased proportionally.
c) The extra tough grade E according to this data sheet is available up to a plate thickness of 200 mm.
Tensile and impact tests will be performed according to EN 10025-6 once per heat and 40 t.
Tests on every heat treatment unit may be possible on request. The test pieces are taken and prepared according to part 1 and 6 of EN 10025.
The tensile test is carried out on specimens of gauge length Lo = 5.65·√So respectively Lo = 5 do, in accordance with EN ISO 6892- 1. Tensile tests according to ASTM A370 may be agreed. The impact test will be carried out on transverse Charpy-V-specimens in accordance with EN ISO 148-1 using a 2 mm striker.
Unless otherwise agreed, the test results are documented in an inspection certificate 3.1 in accordance with EN 10204.
Identification of plates
Unless otherwise agreed, the marking is carried out via steel stamps with at least the following information:
steel grade (S690QL)
number of mother plate and individual plate
the manufacturer’s symbol
inspection representative’s sign
The entire processing and application techniques are of fundamental importance to the reliability of products made from this steel. The user should ensure that his design, construction and processing methods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply with and are suitable for the intended use. The customer is responsible for the selection of the material. The recommendations of the EN 1011 (welding) and CEN/TR 10347 (forming) as well as recommendations regarding job safety in accordance with national rules should be observed.
Cold forming means forming below the maximum allowable stress relief temperature [560 °C (1040 °F)]. S690Q can be cold formed with regard to its high yield strength. Flame cut or sheared edges in the bending area should be ground before cold forming. Cold forming is related to a hardening of the steel and to a decrease in toughness. Some codes may limit the maximum permissible strain during cold forming. Depending on the relevant code this can result in the need of larger bending radiuses than indicated in the chart. For larger cold forming amounts we recommend you to consult the steel producer prior to ordering.
During the processing, the necessary safety measures have to be taken, so that nobody will be exposed to a danger by a possible fracture of the work piece during the forming process.
The following geometries can usually be achieved by cold forming without the formation of surface defects (t is the plate thickness):
|Minimum bending radius||Minimum die width|
|Transverse direction||2 t||7 t|
|Longitudinal direction||3 t||9 t|
If the temperature of 560 °C (1040 °F) is exceeded, the initial tempering can be altered so that the mechanical properties are affected. To regain the initial properties new quenching and tempering become necessary. However, water quenching of a formed workpiece or component will often be less effective than the original quenching in the plate mill so that the fabricator may not be able to reestablish the properties required and therefore hot forming may not be suitable. In this respect we recommend you to contact the steel producer prior to ordering, in all cases where hot forming is required.
Finally, it is the fabricator’s responsibility to obtain the required values of the steel through an appropriate heat treatment.
Flame cutting and welding
Due to its high yield strength, S690QL requires special care during plate processing. For flame cutting, the following minimum preheating temperatures are recommended: 25 °C (77 °F) for plate thickness up to 20 mm, 50 °C (122 °F) for plate thickness up to 50 mm, 100 °C (212 °F) for plate thickness up to 100 mm, 150 °C (302 °F) for plate thickness up to 200 mm and 180 °C (356 °F) for thicker plates.
For very thick cut parts, a postheating at about 200 °C (390 °F) or a slow cooling, e.g. by covering the cut parts with thermo-blankets for hydrogen effusion and reduction of internal stresses, may be necessary.
For general welding instructions, please consult the EN 1011. In order to ensure that the tensile strength of the weld metal fulfils the requirements of the base metal, the heat input and interpass temperature must be limited during welding. Experience has shown that the welding conditions should be chosen so that the cooling time t8/5 does not exceed 20 seconds. This is applicable when using suitable filler materials of a corresponding yield strength class.
The high yield strength of the base material must be taken into account when choosing the filler materials. It should be considered that increased heat input leads to lower tensile properties in the weld metal. If a stress relieving heat treatment is planned during or after plate processing, this must also be considered when selecting the filler materials. To avoid hydrogen-induced cold cracking, only filler materials, which add very little hydrogen to the base metal, may be used. Therefore, shielded arc welding should be preferred. For manual arc welding, electrodes with basic coating (type HD < 5 ml/100 g in accordance with ISO 3690) and dried according to the manufacturer’s instructions should be used. With increasing plate thickness, increasing hydrogen charge and restraint of the weld, a soaking for hydrogen effusion immediately after welding is recommended.
A stress relief heat treatment can be performed at a maximum temperature of 560 °C (1040 °F) and maximum holding time of 60 minutes without significant impairment of the properties. After a stress relief heat treatment using the specified parameters, the requirements for mechanical and technological properties are met. It has to be specified prior to ordering if higher stress relieving temperatures or longer holding times have to be applied. The verification of appropriate stress relieving parameters for a delivered plate may be possible on request.
General technical delivery requirements
Unless otherwise agreed, the general technical delivery requirements in accordance with EN 10021 apply.
Unless otherwise agreed, the tolerances will be in accordance with EN 10029, with class A for thickness and table 4, steel group H, for the maximum flatness deviation. Smaller flatness deviations may be possible on request prior to order.
Unless otherwise agreed, the specifications will be in accordance with EN 10163-2, class A2.
If not agreed otherwise, S690QL fulfils the requirements of class S1E1 in accordance with EN 10160.
If special requirements, which are not covered in this material data sheet, are to be met by the steel due to its intended use or processing, these requirements are to be agreed before placing the order