S600MC high strength structural steel plate

Product Details:
Place of Origin: China
Brand Name: VANFORGE
Certification: ISO9001:2015, ABS, BV, CCS, DNV GL, NKK
Payment & Shipping Terms:
Minimum Order Quantity: 5 metric tons
Price: Negotiable
Packaging Details: Standard seaworthy packing for export
Delivery Time: 15 days
Payment Terms: L/C, T/T
Supply Ability: 3000 metric tons per month

Detail Information

Material: Low Alloy Steel Process: Hot Rolled
Shape: Flat Plate Surface Treatment: Plain And Smooth
Length: Up To 12000mm
High Light:

structural steel sheet

,

hardened steel plate

Product Description

Description

The high-strength structural steel at 600 MPa

S600MC steel is a hot-rolled structural steel made for cold forming, with a minimum yield strength of 600 MPa for stronger and lighter structures.

S600MC steel meets or exceeds the requirements of EN 10149-2.

Typical applications include a wide range of components and parts, such as demanding load-bearing structures. S600 MC comes in coils, slit coils or cut-to-length sheets.

 

Dimension Range

S600MC steel is available in thicknesses of 2.00-10.00 mm and widths up to 1600 mm as coils, slit coils or cut to length sheets in lengths up to 16 meters.

 

Mechanical Properties

Thickness

(mm)

Yield strength ReH (1)

(min MPa)

Tensile strength Rm

(MPa)

Elongation A80 (2)

(min %)

Elongation A5

(min %)

Min. inner bending radius for a 90° bend (4)
2.00- 3.00 600 650- 820 13 16 (3) 0.7 x t
3.01- 6 600 650- 820   16 1.1 x t
6.01- 10 600 650- 820   16 1.4 x t

The mechanical properties are tested in the longitudinal direction.

(1) If ReH is not applicable then Rp 0.2 is used.

(2) A80 value applies for thicknesses < 3.00 mm

(3) A5 value applies for sheet thickness t ≥ 3mm.

(4) For both longitudinal and transverse direction.

 

Impact Properties

Grade Min. impact energy for longitudinal testing, Charpy V 10x10 mm test specimens
S600MC D 40 J/-20 °C
S600MC E 27 J/-40 °C

Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 6mm. The specified minimum value corresponds to a full-size specimen.

 

Chemical Composition (ladle analysis), %, max.

C Si Mn P S Al Nb V Ti
0.12 0.21 1.90 0.025 0.010 0.015 0.09 0.20 0.15

(1) If the material is to be hot-dip galvanized according to category A or category B in EN 10149-2 this must be specified at the time of order. Other galvanizing classes with higher Si-content are available after agreement.

(2) Sum of Nb, V and Ti = max 0.22%

The steel is grain refined.

 

Thickness

Tolerances according to EN 10051.

 

Length and Width

Width and length tolerances according to EN 10051. Length tolerances only apply for cut to length sheets.

 

Shape

Tolerances according to EN 10051. Narrower tolerances are available on request.

 

Flatness

Tolerances according to EN 10051.

Flatness guarantees only apply for cut to length sheets.

 

Surface Properties

According to EN 10163-2 Class A, Subclass 3.

 

Delivery Conditions

Thermomechanically Rolled. S600MC steel is available in as rolled or pickled surface condition with mill or cut edge.

 

Fabrication and Other Recommendations

Welding, bending and machining

S600MC steel has good welding, cold forming and cutting performance.

S600MC steel is a cold forming steel not suited for heat treatments at temperatures above 580°C since the material then may lose its guaranteed properties.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the product.

 

Specification

Plate thickness: 4-100mm

Width: 500mm – 4700mm

Length: On request

 

Production process

S600MC high strength structural steel plate 0

 