S1100 plus high yield strength quenched and tempered structural steel plate

Product Details:
Place of Origin: China
Brand Name: VANFORGE
Certification: ISO9001:2015, ABS, BV, CCS, DNV GL, NKK
Payment & Shipping Terms:
Minimum Order Quantity: 5 metric tons
Price: Negotiable
Packaging Details: Standard seaworthy packing for export
Delivery Time: 15 days
Payment Terms: L/C, T/T
Supply Ability: 3000 metric tons per month

Detail Information

Material: Low Alloy Steel Process: Hot Rolled
Shape: Flat Plate Surface Treatment: Plain And Smooth
Length: Up To 12000mm
High Light:

structural steel sheet

,

hardened steel plate

Product Description

Description

S1100 Plus steel is a hot-rolled structural steel with a minimum yield strength of 1100 MPa. The material feature excellent flatness and surface quality, providing an outstanding finish to the final products. Typical applications include a wide range of parts and components such as demanding load-bearing structures.

 

S1100 Plus steel benefits

  • Exceptional weldability with matching strength, elongation and toughness across a weld
  • Very good bendability and surface quality
  • Superior consistency guaranteed by close tolerances
  • High impact toughness which provides for good resistance to fractures

 

Dimension Range

S1100 Plus steel is available as cut to length sheets in thicknesses of 4.0 - 8.0 mm. S1100 Plus is available in widths up to 1600 mm and lengths up to 13 000 mm depending on thickness. Please contact your sales representative for more information regarding dimensions.

 

Mechanical Properties

Thickness

(mm)

Yield strength Rp0.2

(min MPa)

Tensile strength Rm

(MPa)

Elongation A

(min %)

Min. inner bending radius for a 90° bend
4.0 - 6.0 1100 1130 - 1350 10 3.5 x 1
6.1 - 8.0 1100 1130 - 1350 10 4.0 x 1

The mechanical properties are tested and guaranteed in both longitudinal and transverse direction.

 

Impact Properties

Test direction Min. Impact energy for Charpy V 10x10 mm test specimens
Longitudinal 27 J/ -40 °C
Transverse 27 J/ -20 °C

Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 6mm. For thicknesses between 6.0 - 8.0 mm, sub-size Charpy V-specimens are used. The specified min value is then proportional to the cross-sectional area of the specimen compared to a full-size specimen (10x10 mm).

 

Chemical Composition, %, max

C Si Mn P S Al
0.20 0.50 1.80 0.020 0.005 0.015

 

Thickness

Tolerances meet the requirements of EN 10 051, but offer considerably narrower tolerances.

 

Length and Width

Width and length tolerances meet the requirements of EN 10051, but offer narrower tolerances.

 

Shape

Tolerances according to EN 10051. Narrower tolerances according to the VANFORGE standard are available on request.

 

Flatness

Flatness meets the requirements of EN 10051, but offer considerably narrower tolerances.

 

Surface Properties

According to EN 10 163-2 Class A, Subclass 3.

 

Delivery Conditions

S1100 Plus steel is supplied in as rolled surface condition, primer coated surface is available on request. The delivery condition is Quenched and Tempered.

 

Fabrication and Other Recommendations

Welding, bending and machining

S1100 Plus steel has extremely good weldability with the same minimum guarantees for strength, elongation and impact toughness across a weld as in the parent material, as long as our recommendations are followed.

 

S1100 Plus steel has good forming performance.

 

S1100 Plus steel has obtained its mechanical properties by quenching and subsequent tempering. The properties of the delivery condition cannot be retained after exposure to temperatures in excess of 400 °C.

 

Appropriate health and safety precautions must be taken when welding, cutting, grinding or otherwise working on this product. Grinding, especially of primer coated plates, may produce dust with a high particle concentration.

 

Specification

Plate thickness: 4-100mm

Width: 500mm – 4700mm

Length: On request

 