Fine Grain Quenched And Tempered Steel Plate Hot Rolled For Sour Gas Service
|Place of Origin:||China|
|Certification:||ISO9001:2015, ABS, BV, CCS, DNV GL, NKK|
Payment & Shipping Terms:
|Minimum Order Quantity:||5 metric tons|
|Packaging Details:||Standard seaworthy packing for export|
|Delivery Time:||15 days|
|Payment Terms:||L/C, T/T|
|Supply Ability:||3000 metric tons per month|
|Material:||Low Alloy Steel||Process:||Hot Rolled|
|Shape:||Flat Plate||Surface Treatment:||Plain And Smooth|
|Length:||Up To 12000mm||Condition:||Quenched And Tempered|
heavy steel plate,
bulletproof steel plate
600HBW quenched high hardness alloy steel ballistic plate
The ballistic protection steel with extra-high hardness
600HBW ballistic steel is a ballistic protection steel of extra-high hardness, nominal 600 HBW, available in thicknesses of 3‑6 mm (0.118‑0.236″).
600HBW ballistic steel is available as cut-to-length sheet in thicknesses of 3‑6 mm (0.118‑0.236″). Delivered in quenched condition, 600HBW ballistic steel is not intended for further heat treatment.
600HBW ballistic steel is available as cut-to-length sheet in thickness between 3.0 - 6.0 mm.
|3.0 – 6.0||570 - 640|
Brinell hardness test according to EN ISO 6506-1 on each heat treatment individual/coil.
Hardness is measured on a milled surface 0.3 - 2 mm below plate surface.
Chemical Composition (ladle analysis), %, max
The steel is grain-refined.
Phosphorous and sulphur are not intentionally alloying elements.
(Min / Max)
|Cut Length||3.00 - 4.00||- 0.0 / + 0.36|
|Cut Length||4.01 - 5.00||- 0.0 / + 0.40|
|Cut Length||5.01 - 6.00||- 0.0 / + 0.42|
Length and Width
Sheets are delivered with mill edges cut as standard.
• Tolerances conform to EN 10 051 or to VANFORGE´s standard after agreement.
Tolerances according to EN 10029 Class N (steel type L)
|Cut Length||3.00 - 4.00||6|
|Cut Length||4.01 - 5.00||6|
|Cut Length||5.01 - 6.00||6|
Tolerances according to EN 10051.
According to EN 10163-2 Class B Subclass 3
600HBW ballistic steel is delivered in quenched condition.
Fabrication and Other Recommendations
Welding, bending and machining
600HBW ballistic steel is not intended for further heat treatment. If 600HBW ballistic steel is heated above 150 °C after delivery from VANFORGE no guarantees for the properties are given.
Appropriate health and safety precautions must be taken when cutting, welding, grinding or otherwise working on the product. Grinding, especially of primer coated plates, may produce dust with high particle concentration.