330HBW Hardened Engineering Solid Steel Bar , Hot Rolled Bar 275 - 325HBW

Product Details:
Place of Origin: China
Brand Name: VANFORGE
Certification: ISO9001, ISO10012, ISO14001, OHSAS18001, ABS, BV, DNV, Lloyd, NK
Payment & Shipping Terms:
Minimum Order Quantity: 5 metric tons
Price: Negotiable
Packaging Details: Seaworthy package for export
Delivery Time: 60 days
Payment Terms: L/C, T/T
Supply Ability: 5000 metric tons per month

Detail Information

Material: Alloy Steel Process: Hot Rolled
Treatment: Quenched And Tempered Surface: Black, Peeled
Shape: Round Length: Cut To Length On Request
High Light:

solid steel bar

,

hardened steel rod

Product Description

330HBW hardened tool and engineering steel round bar

 

Description

Pre-hardened, precise, predictable steel, now in round bars

330HBW tool steel round bars are pre-hardened, ready-to-use quenched and tempered tool steels that come in a wide range of diameters from small to large.

Suitable for engineering applications in tool holders and in different types of shafts and rolls, the diameter dimensions also provide a better solution for round parts in tooling applications like molding and in dies for aluminium die casting.

 

Dimension Range

330HBW tool steel round bars are available in diameters 21 - 141 mm. Other dimensions can be available on request.

 

Mechanical Properties

Diameter

(mm)

Hardness

(HBW)

21 - 141 275 - 325

Hardness is measured, according to EN ISO 6506-1, on a milled surface 0.5 - 2 mm below the plate surface.

Bar Hardness is measured on a milled surface, with indents positioned as impact test according to EN 10083.

 

Impact Properties

Test temperature Impact energy, Charpy-V, Min J
20 °C 35 min J

Impact testing according to EN 10083.

 

Ultrasonic testing

Ultrasonic inspection is carried out according to EN 10308.

 

Diameter and Length

Tolerances according to EN 10060.

 

Straightness

Straightness according to EN 10060.

 

Surface Properties

Peeled surface.

 

Delivery Conditions

Quenched and Tempered at a minimum temperature of 590 °C.

On delivery from VANFORGE the plates meet the following specifications:

  • free from mill scale
  • not repair welded

 

Fabrication and Other Recommendations

Welding, bending and machining

330HBW tool steel is not intended for further heat treatment. If 330HBW tool steel is heated above 590 °C after delivery from VANFORGE no guarantees for the properties of the steel are given.

Nitriding or surface coating may be carried out if the temperature is below 590 °C.

Appropriate health and safety precautions must be taken when welding, cutting, grinding or otherwise working on the product. Grinding, especially of primer coated plates, may produce dust with high particle concentration.

 

Product size range

Diameter: 21mm - 141mm

Length: on request

 

 

Production Process

 

330HBW Hardened Engineering Solid Steel Bar , Hot Rolled Bar 275 - 325HBW 0

330HBW Hardened Engineering Solid Steel Bar , Hot Rolled Bar 275 - 325HBW 1

 

 

Key clients

 

330HBW Hardened Engineering Solid Steel Bar , Hot Rolled Bar 275 - 325HBW 2

 

 

Get in touch with us

Enter Your Message

You Might Be Into These