2378X CrMnNiMo Quenched And Tempered Steel Plate Excellent Machinability

Product Details:
Place of Origin: China
Brand Name: VANFORGE
Certification: ISO9001:2015, ABS, BV, CCS, DNV GL, NKK
Payment & Shipping Terms:
Minimum Order Quantity: 5 metric tons
Price: Negotiable
Packaging Details: In bundles, standard seaworthy packing for export
Delivery Time: 15 days
Payment Terms: L/C, T/T
Supply Ability: 3000 metric tons per month

Detail Information

Material: Alloy Steel Process: Hot Rolled
Shape: Flat Plate Surface Treatment: Plain And Smooth
Length: Up To 12000mm Condition: Quenched And Tempered
Application: Molds And Tooling Feature: Excellent Polishability And Machinability
High Light:

bulletproof steel plate

,

tool steel plate

Product Description

2738X MOULD STEEL is a prehardened CrMnNiMo-alloyed tool steel for the construction of plastic molds with superior surface requirements on molds. It is characterized by excellent polishability, photoetchability, spark erosion behavior and dimensional stability as well as good machinability.
 
Product description
Designation and range of application
2738X MOULD STEEL is a modified version of 1.2738 according to AISI and ASTM A681. Compared to DIMO 2738, 2738 MOULD STEEL has, as a result of its adjusted chemical analysis, higher hardness values in the delivery condition which result in higher service lifetime of the mold even if using the steel without heat treatment.
 
2738X MOULD STEEL is available as plate with sheared or flame cut edges in the following dimensions:

Thickness≥ 12 ≤ 130 mm≥ 1/2 ≤ 5 inch> 130 ≤ 165 mm> 5 ≤ 6 1/2 inch
Width (1)≥ 1000 ≤ 2500 mm≥ 40 ≤ 98 1/4 inch≥ 1000 ≤ 2050 mm≥ 40 ≤ 80 1/2 inch
Length≥ 4500 ≤ 6000 mm≥ 177 1/2 236 inch≥ 4000 ≤ 6000 mm≥ 157 1/2 ≤ 236 inch

(1) Widths < 1250 mm (49 in) have to be ordered with an even number of plates
Other dimensions available upon request.
 
Production
The 2738X MOULD STEEL production route is designed to achieve the excellent properties of this mold steel type with superior surface requirements. 2738 MOULD STEEL is characterized by high dimensional stability. The 2738 MOULD STEEL production route provides excellent polishability, photoetchability and spark erosion properties. Therefore 2738 MOULD STEEL is particularly suitable for molds with superior surface requirements if suitable manufacturing processes are employed.
 
The good sulfidic and oxidic cleanliness and the modification of the few remaining inclusions by the calcium treatment lead to good machinability and minimize the tool wear.
 
These properties can only be achieved by the combination of the following 2738X MOULD STEEL-production steps:
· desulphurization to S ≤ 0.002 % for high sulfidic cleanliness
· chemical analysis in dependence of dimensions
· vacuum degassing
· argon stirring for high sulfidic and oxidic cleanliness
· calcium treatment for inclusion shape control
· special casting conditions to assure the high cleanliness and homogenity
· High Shape Factor Rolling (high thickness reduction) to realize a closely packed structure
· appropriate heat treatment parameters according to analysis and dimensions to assure homogeneous hardness distribution over the plate and to minimize residual stresses
 
Chemical composition

CSiMnPSCrMoNiV
0.30-0.40≤0.401.40-1.60≤0.020≤0.0021.00-1.400.30-0.600.30-0.60≤0.30

(1) alloyed depending on dimensions
 
Delivery condition
2738X MOULD STEEL is supplied in the prehardened (air hardened + tempered) condition.
Mechanical and technological properties in the delivery condition
 
Hardness
Unless otherwise agreed the hardness at the surface in the delivery condition is 320 - 370 HB. According to EN 18265, table B2, this corresponds to a tensile strength of approximately 1015 - 1175 MPa (146 - 169 ksi).
 
Testing
· Heat analysis
· Dimension control
· Surface inspection
· Hardness
The hardness (HB) is tested on surface of each rolled mother plate.
· Ultrasonic testing
Unless otherwise agreed, 100 % ultrasonic testing is performed on each plate in the delivery condition in accordance with ASTM A 578, Level C, supplementary requirements S1 and S9.
Upon request, the ultrasonic testing in accordance with EN 10160.is possible. As admissible limit applies quality class 4 in table 5 of EN 10228-3. In this case the desired testing type has to be indicated on the order.
 
Unless otherwise agreed, the results are documented in an inspection certificate 3.1 in accordance with EN 10204.
 
Identification of plates
Unless otherwise agreed the marking is carried out via steel stamps with at least the following information:
· steel grade (2738X MOULD STEEL)
· heat number
· number of mother plate and individual plate
· the manufacturer’s symbol
· inspector’s sign
 
Processing
Heat treatment
2738X MOULD STEEL is delivered in the prehardened condition; therefore further heat treatment is generally not necessary. This avoids the risks and costs involved by the hardening and tempering of a mold after processing. Should a heat treatment become necessary, the following data are recommended:

soft annealingstress relievingPreheating before hardeninghardeningtempering

720 - 740 °C (1330 - 1360 °F) 2 - 4 h,

furnace cooling

hardness about 230 HB

in the delivery condition max.

580 °C (1080 °F)

1 - 2 h,

furnace cooling

 

450 - 650 °C (840 - 1200 °F)

 

840 - 860 °C (1540 - 1580 °F)/oil; for low wall thicknesses warm bath hardening at 200 - 230 °C (390 - 450 °F) is possiblein accordance with tempering diagram to required hardness (min. 1 h/25 mm (1 in) wall thickness)

 
General technical delivery requirements
Unless otherwise agreed, the general technical delivery requirements in accordance with EN 10021 apply.
 
Tolerances
Unless otherwise agreed, tolerances are in accordance with EN 10029 / ASTM A 6 with the following restrictions:

plate thickness:in accordance with EN 10029, class C
plate width:≥1000 mm≤1500 mm±25 mm≥40≤59 in±1 in
 >1500 mm≤2050 mm±40 mm>59≤80 1/2 in±1 1/2 in
 >2050 mm±50 mm>80 1/2 in±2 in
plate length: ± 1000 mm ± 40 in
flatness:≤3 mm/m

Unless otherwise agreed, short lengths ≥2 m (79 in) are part of the delivery.
 
Surface quality
Unless otherwise agreed, the specifications will be in accordance with EN 10163-2 class A, subclass 3. Shot blasting of upper and lower surface of the plate and shop priming are possible on request.
 
General note
If special requirements, which are not listed in this specification, are to be met by the steel due to its intended use or processing, these requirements are to be agreed before placing the order.
 
 
Production process
2378X CrMnNiMo Quenched And Tempered Steel Plate Excellent Machinability 0
 
2378X CrMnNiMo Quenched And Tempered Steel Plate Excellent Machinability 1
 
 

Get in touch with us

Enter Your Message

You Might Be Into These